A283/Q195 Cold Rolled Steel Coil
A283 steel coil exhibits excellent work hardening properties during cold forming for its high strength and plasticity. After repeated cold working deformation, the coil can still show similar strength and hardness, with even better ductility and toughness. In addition, due to its good welding performance, the coil can be easily welded into parts of various shapes and sizes, and the welding quality is stable and reliable. A283 steel coils are widely used in the manufacturing of various mechanical parts, such as bolts, nuts, pins and other standard parts as well as various non-standard mechanical parts. In addition, they are also used in the manufacture of building structural materials.
Product Description
|
Product Name |
A283/Q195 Cold Rolled Steel Coil |
|
Production Process |
Hot Rolling, Cold Rolling |
|
Material Standards |
AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
|
Width |
45mm-2200mm |
|
Length |
Custom Size |
|
Thickness |
Hot Rolling: 2.75mm-100mm |
|
Delivery Conditions |
Rolling, Annealing, Quenching, Tempered or Standard |
|
Surface Process |
Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
|
A283 |
Cmax. |
Mnmax. |
Pmax. |
Smax. |
Si (Greater1 inch, less than 1/2 inch) |
Si (Greater 1/2 inch) |
Cumin. |
|
Grade A |
0.14 |
0.90 |
0.035 |
0.04 |
0.40 |
0.15-0.40 |
0.20 |
|
Grade B |
0.17 |
0.90 |
0.035 |
0.04 |
0.40 |
0.15-0.40 |
0.20 |
|
Grade C |
0.24 |
0.90 |
0.035 |
0.04 |
0.40 |
0.15-0.40 |
0.20 |
|
Grade D |
0.27 |
0.90 |
0.035 |
0.04 |
0.40 |
0.15-0.40 |
0.20 |
Mechanical Properties
|
A283 |
Tensile Strength |
Yield Strength min. |
Elongation Rate 8 inches |
Elongation Rate 2 inches |
||
|
Grade A |
45000-60000 psi |
310-415 MPa |
24000 psi |
165 MPa |
27 % min. |
30 % min. |
|
Grade B |
50000-65000 psi |
345-450 MPa |
27000 psi |
185 MPa |
25 % min. |
28 % min. |
|
Grade C |
55000-75000 psi |
380-515 MPa |
30000 psi |
205 MPa |
22 % min. |
25 % min. |
|
Grade D |
60000-80000 psi |
415-550 MPa |
33000 psi |
230 MPa |
20 % min. |
23 % min. |
Physical Performance
|
Physical Performance |
Metric |
Imperial |
|
Density |
7.80 g/cc |
0.282 lb/in³ |
Scope of Application
ASTM A283 steel plate is a kind of low carbon steel with high strength and
good formability. It is easy to process and manufacture, and can be safely
welded by various welding methods. ASTM A283 steel plate is a structural carbon
steel plate used for low or medium tensile strength applications. ASTM A283
steel plate is used in the manufacture of riveted, bolted and welded structures
for storage tanks and cryogenic control vessels, bridges and buildings,
including prefabricated buildings, warehouses and industrial commercial
structures.
Related products
-
304 Stainless Steel Plate
Contact Us304 stainless steel plate is one of the most popular steel plates across the globe for a mix of its favorable characteristics. 304 stainless steel is mainly composed of iron, chromium and nickel. This combination leads to outstanding oxidation resistance and corrosion resistance of 304 stainless steel plates. 304 stainless steel is a versatile stainless steel material with stronger anti-rust properties than 200 series stainless steel materials. It is also better in terms of high temperature resistance. The 304 stainless steel plate has a smooth surface, high plasticity, toughness and mechanical strength, and is resistant to corrosion by acids, alkaline gases, solutions and other media. Due to its good versatility and relatively low cost, 304 stainless steel plate is widely used in food processing equipment, building materials, automobile parts and other fields.